The development of modern, high-efficiency steam turbines has led to an increase in deposition, erosion, and corrosion problems.Close tolerances in the turbines, the use of high-strength steels, and impure steam all contribute to these conditions.Although several factors influence the formation of deposits on turbine components, the general effect is the same no matter what the cause.Adherent deposits form in the steam passage, distorting the original shape of turbine nozzles and blades.These deposits, often rough or uneven at the surface, increase resistance to the flow of steam.Distortion of steam passages alters steam velocities and pressure drops, reducing the capacity and efficiency of the turbine.Where conditions are severe, deposits can cause excessive rotor thrust.Uneven deposition can unbalance the turbine rotor, causing vibration problems.As deposits accumulate on turbine blades, stage pressures increase.Figure 18-1 shows the effect of gradual deposit buildup on stage pressure.

The deposits were caused by the use of contaminated water to attemperate the steam.In a fouled condition, this 30-MW turbine lost over 5% of its generating capacity.Turbine deposits can accumulate in a very short time when steam purity is poor.The turbine shown in Figure 18-2 was forced off-line by deposition only 3 months after it was placed in operation.Carryover of boiler water, resulting from inadequate steam-water separation equipment in the boiler, caused this turbine deposit problem.The nature of silica deposits found on turbine blades varies greatly.Table 18-1 lists a number of silica compounds that have been identified in various studies of turbine blade deposition.Of these, amorphous silica (SiO2) is the most prevalent.Causes of Turbine Deposition Some mechanical entrainment of minute drops of boiler water in the steam always occurs.When this boiler water carryover is excessive, steam-carried solids produce turbine blade deposits.

The accumulations have a composition similar to that of the dissolved solids in the boiler water.Priming and foaming are common causes of high levels of boiler water carryover.vicks vaporizer taurangaBecause of the high levels of carryover often encountered, these conditions often lead to superheater tube failures as well.vicks vaporizer taurangaTurbine deposits are also caused by the use of impure water for steam attemperation and by leakage in closed heat exchangers used for attemperation.vaporizer tullenIf a boiler produces pure steam and turbine deposits still occur, the attemperating system should be investigated as a possible source of contamination.e cigarette humidite

Attemperating water should be of the same purity as the steam.Any chemical treatment in the attemperating water should be volatile.Another source of turbine deposition is the vaporization of salts present in boiler water.e cigarette contentsWith the exception of silica, vaporization of boiler water salts is usually not significant at pressures below 2400 psig.e cigarette ballwin moSilica can vaporize into the steam at operating pressures as low as 400 psig.vaporizer tuscaloosaThis has caused deposition problems in numerous turbines.vaporizer store tustinThe solubility of silica in steam increases with increased temperature; therefore, silica becomes more soluble as steam is superheated.tuzkovy vaporizer

As steam is cooled by expansion through the turbine, silica solubility is reduced and deposits are formed, usually where the steam temperature is below that of the boiler water.volcano vaporizer tweedehandsTo minimize this problem, the quantity of silica in the steam must be controlled.fender vaporizer tweedehandsSilica deposits are not a problem in most turbines where the silica content in the steam is below 0.02 ppm.titan ii vaporizerTherefore, it has become customary to limit silica to less than 0.02 ppm in the steam.vaporizer pen typesSometimes, because of the more stringent operating conditions of certain turbines, vendors specify that steam silica be maintained at less than 0.01 ppm.vaporizer ulovlig

vaporous silica carryover occurs have been thoroughly investigated and documented.Researchers have found that for any given set of boiler conditions using demineralized or evaporated quality makeup water, silica is distributed between the boiler water and the steam in a definite ratio.ultrasonic vaporizer transducerThis ratio, called the distribution ratio, depends on two factors: boiler pressure and boiler water pH.vaporizer under 30The value of the ratio increases almost logarithmically with increasing pressure and decreases with increasing pH.pax vaporizer unboxingThe effect of boiler water pH on the silica distribution ratio becomes greater at higher pH values.solo vaporizer unboxing

A pH increase from 11.3 to 12.1 reduces the ratio by 50%, while a pH increase from 7.8 to 9.0 has no measurable effect.For any boiler pressure and pH, the distribution ratio for silica can be determined from Figure 18-3.pax vaporizer unhealthyThe amount of silica vaporized with the steam can be determined by measurement of boiler water silica.unic vaporizerThe proper boiler water silica level necessary to maintain less than 0.02 ppm silica in the steam is shown in Figure 18-4.vaporizer unter 100 euroWhen soluble, the silica present in boiler feedwater does not influence the amount of silica present in the steam.pax vaporizer update

When added to boiler water in separate experiments, equivalent quantities of silicic acid and sodium silicate produced the same amount of silica in the steam.firefly vaporizer usb chargerBecause the amount of silica in the steam is greatly affected by pH, it is likely that silicic acids are involved in the vaporization mechanism.vaporizer use for coldsSilica has a higher solubility in superheated steam than in saturated steam for any given pressure.vaaapp vaporizer ev101If mechanical carryover contributes to the silica content of the saturated steam, the silica will be dissolved during superheating, provided that the total silica present does not exceed the solubility of silica in the superheated steam.eclipse vaaapp vaporizer

Therefore, silica deposits are seldom found in superheater sections of a boiler.After steam reaches a turbine it expands, losing pressure and temperature.vaporizer vamo v5As a result, the solubility of the silica decreases.vaporizer vanillaStudies have shown that with a maximum of 0.02 ppm of silica in the steam, a pressure of less than 200 psig is reached in the turbine before silica starts to condense from the steam.vaporizer vapor brothersTherefore, silica preferentially deposits in the intermediate-pressure and low-pressure sections of the turbine where the specific volume of the steam varies from approximately 1 to 10 ft3/lb.vaporizer variable voltage battery

Solubility data shown in Figure 18-5 helps to explain the distribution of silica deposits in the turbine.Turbine deposits are also formed where localized silica saturation occurs and silica condenses from the steam in those areas of the turbine.vaporizer variable wattagePartial evaporation of the precipitated silica can then occur with only a portion of the silica being dissolved by the continuous steam flow.vaporizer vasarlasDeposits remain as a result.vaporizer vaultAnother factor affecting the location of turbine deposits is the velocity in the turbine.vaporizer venice beachSteam flows from the inlet to the outlet of the turbine in only a fraction of a second.vea vaporizer

Consequently, deposition is shifted downstream from the saturation point by the high steam velocities.Prevention of Silica Deposits The most significant factor in minimizing turbine silica deposits is the maintenance of low silica concentrations in the boiler water.vaporizer vegasExternal treatment equipment must be operated carefully to limit the amount of silica entering with the makeup water, and the condensate must be monitored to minimize contamination.plume veil vaporizerAfter silica enters the boiler water, the usual corrective action is to increase boiler blowdown (to decrease the boiler water silica to acceptable levels) and then to correct the condition that caused the silica contamination.silver surfer vaporizer veil of maya

When a turbine becomes fouled with water-soluble salts as a result of boiler water carryover or attemperating water contamination, turbine capacity can often be restored by water washing.vetta vaporizer reviewBecause it can cause severe turbine damage, water washing should be supervised carefully and the recommendations of the turbine vendor should be followed.volcano vaporizer video demoWhen the turbine becomes fouled with compounds that are not water-soluble (including silica), water washing rarely restores capacity.vaporizer mountain viewOut-of-service cleaning by blasting with aluminum oxide or other soft grit material is required to remove these deposits.viking vaporizer parts

Erosion of turbine blades results in rough, uneven surfaces that alter steam flow paths.This reduces turbine efficiency and can also limit capacity.grasshopper vaporizer vimeoErosion at the high-pressure end of a turbine is usually caused by solid particles (usually iron oxide) present in the steam.violin vaporizerIron oxide particles are present if they were not removed by steam blows during system start-up.vaporizer viperThey can also result from exfoliation of superheater or main steam header oxides or can be introduced into the steam by contaminated attemperating water.vip1 vaporizerErosion of intermediate and low-pressure blades is usually caused by water in the steam.vaporizer vivid

Operation below design inlet steam temperature or at low load can cause condensation in these stages, leading to erosion problems.virgin vaporizerCarbon dioxide or other acidic species present in the condensate can accelerate the damage.vaporizer shop virginia beachSome protection against erosion-corrosion can be provided by low distribution ratio amines, which neutralize the acidity and elevate the pH of the condensate.vaporizer laws in virginiaPitting, corrosion fatigue, and stress corrosion cracking problems all occur in steam turbines.vintage vaporizer valueThe major corrodents are sodium hydroxide, chloride, sulfate, and sulfides.vizy vaporizer

Usually, the level of contaminants present in steam is not high enough to corrode the system components.As steam expands through a turbine, the solubility of contaminants in the steam decreases.vizy vaporizer vancouverThey condense onto surfaces at solution concentrations much higher than the original contaminant concentration in the steam.vizipipa vaporizerThese concentrated solutions promote system corrosion.volatizer vm2 vaporizerPitting is commonly associated with chloride deposits and occurs on rotors, disks, and buckets.volatizer vm3 vaporizerPitting attack often occurs when a moist, oxygen-laden atmosphere develops in out-of-service turbines.volcano vaporizer vodka

Damage is most severe when chloride deposits are also present.An oxygen-free or condensate-free atmosphere should be maintained to protect out-of-service turbines from corrosion.vaporizer v6 von hannets®The problems are most common in low-pressure sections of large power plant turbines, which are characterized by high stresses, crevices, and operating temperatures conducive to the condensation of concentrated solutions of steam contaminants.volcano vaporizer von vapormedProblems also occur in high-pressure sections and smaller industrial-sized turbines, usually when substantial levels of steam contamination occur.sapphyre voyager vaporizer reviewsThese problems can be mitigated by designs that prevent crevices, lower stresses, and/or employ lower-strength materials.vo2 vaporizer reviews